項(xiàng)目Property |
單位Unit |
檢測(cè)方法Test method |
SCH900系列（透明） |
|
結(jié)構(gòu)Structure |
|
|
FEVE/PET/FEVE |
|
A面含氟層厚度Side A thickness |
μm |
GB/T 6672-2001 |
15 |
|
PET厚度Thickness |
μm |
GB/T 6672-2001 |
250-300 |
|
B面含氟層厚度 Side B thickness |
μm |
GB/T 6672-2001 |
15 |
|
產(chǎn)品總厚度 Total thickness |
μm |
GB/T 6672-2001 |
280-320 |
|
拉伸強(qiáng)度(TD) Tensile strength |
N/10mm |
ASTM D882-2002 |
≥120 |
|
拉伸強(qiáng)度(MD) Tensile strength |
N/10mm |
ASTM D882-2002 |
≥120 |
|
拉伸率(MD) Elongation |
% |
ASTM D882-2002 |
≥100 |
|
拉伸率(TD) Elongation |
% |
ASTM D882-2002 |
≥90 |
|
熱收縮率(MD) Shrinkage |
% |
ASTM D1204-2002 |
≤1.0 |
|
熱收縮率(TD) Shrinkage |
% |
ASTM D1204-2002 |
≤0.5 |
|
層間附著力(FEVE/PET) Coat adhesion |
級(jí) |
GB/T9286-1988 |
0 |
|
涂層與EVA剝離強(qiáng)度(初始) Peel strength |
N/10mm |
GB/T2790-1995 |
>40 |
|
涂層與EVA剝離強(qiáng)度(85℃/85% 1000小時(shí)) Peel strength |
N/10mm |
GB/T2790-1995 |
>40 |
|
水蒸氣透過率 Water vapor transmittance |
g/m2·day |
ASTM F1249-2006 |
<2.5 |
|
局部放電電壓 Partial discharge |
VDC |
IEC60664-1-2007 |
≥1000 |
|
擊穿電壓強(qiáng)度 Breakdown voltage |
KV |
ASTM D149-1997 |
≥18 |
|
色差變化(85℃/85% 1000小時(shí)) Color change |
⊿E |
GB/T 11186.3-1989 |
2.0 |
供應(yīng)商參考報(bào)價(jià)：面議
太陽能光伏：
{try{}catch(e){}var f='http://service.weibo.com/share/share.php?',u=d.location.href,p=['url=',e(u),'&title=',e(encodeURIComponent('#新能源產(chǎn)品推薦#【透明背板 — 上海創(chuàng)輝膜技術(shù)有限公司】SCH900系列透明背板，背板不會(huì)產(chǎn)生反光現(xiàn)象，適合應(yīng)用于公路、鐵路、機(jī)場(chǎng)等嚴(yán)格防眩光需求的環(huán)境。..')),'&appkey=1803333894','&pic=http://file.china-nengyuan.com/999/product/small/201306/p670058001372382766.jpg'].join('');function a(){if(!window.open([f,p].join(''),'mb',['toolbar=0,status=0,resizable=1,width=620,height=450,left=',(s.width-620)/2,',top=',(s.height-450)/2].join('')))u.href=[f,p].join('');};if(/Firefox/.test(navigator.userAgent)){setTimeout(a,0)}else{a()}})(screen,document,encodeURIComponent));){kind=link}